Active filters
Coextrusion Blown & castReset filtersCoextrusion Blown & cast
Multilayer blown film are currently used in miscellaneous packaging applications such as modified atmosphere packaging, shrinkable films, barrier lidding films, vacuum bags, stand-up pouches and skin packaging. Orevac® resins are designed as tie layers to bond to barrier materials such as... Read more
-
ion-typemelt-index-g-10min-190c-2-16kgmelting-point-cvicat-softening-point-capplication
-
IONIA™ 2610
Zn5.29878Film, Extrusion coating -
Comonomer content (%)Melt index (g/10 min,190°C)Melting point (°C)Vicat (°C)Flexural modulus (MPa)
-
LOTRYL® BESTPEEL 2008
2077946- -
Base PolymerReactivityMelt index (g/10 min,190°C)Melting point (°C)Vicat (°C)Density (g/cm3)
-
OREVAC® 18300
LLDPE++2.3120850.91 -
OREVAC® 18302N
LLDPE++1.5123840.91 -
Base PolymerReactivityMelt index (g/10 min,190°C)Melting point (°C)Vicat (°C)
-
LOTADER® 18603T
EMA++3.592< 40 -
Base PolymerReactivityMelt index (g/10 min,190°C)Melting point (°C)Vicat (°C)Density (g/cm3)
-
OREVAC® 18341
LLDPE++++1.5121950.92 -
OREVAC® 18362
LLDPE+2.5123950.92 -
OREVAC® PP 18722
Random PP+71431200,90 -
OREVAC® PP 18729
Homo PP+4,51621370,90 -
Vinyl acetate content (%Wt)MAH content (%)Melt index (g/10 min,190°C)Melting point (°C)Vicat (°C)
-
LOTADER® 9304T
VA (25)0.27.58049 -
LOTADER® 9305T
VA (28)0.618068< 40 -
Ethylene content (%mol)Melt index (g/10 min,190°C)Melt index (g/10 min,210°C)Melting point (°C)O2 Trans. rate (65% RH,20°C, cm3.20µm/m².24hrs.atm)
-
EVASINTM EV 4451V
441,8-1651,8